Structural Wood Adhesive
Thixotropic structural paste for wood bonding and fillet joints.
A thixotropic structural adhesive paste for fillet joints on wood and composites, and for general structural wood bonding. It stays put on vertical and overhanging surfaces and is still easy to apply and smooth. It cures at room temperature, copes with high humidity, and comes with standard and fast hardeners you can blend for any working time in between.
Datasheets available on request
Key benefits
- 60% bio-based carbon in the resin part, the highest in the range*
- No sag on vertical or overhead surfaces
- Cures at room temperature, copes with high humidity
- Standard and fast hardeners; blend them for anything in between
Pack sizes
1.25, 4.75 and 20 kg kits
Supplied to order: contact us for stock and lead times.
Pairs with
Specifications
| Mix ratio | 100 : 25 (4 : 1) by weight |
|---|---|
| Gel time | 1 h 51 min standard, 24 min fast |
| Use above | 10 °C |
| Cure | Room temperature |
| Apply with | Round trowel, squeegee or spatula |
| Sag | None on vertical walls |
| Bio-based carbon* | 60% resin part, 52% mixed |
* Bio-based carbon is the share of carbon atoms that come from plant sources rather than fossil sources. "Resin part" is Part A on its own; "mixed" covers resin and hardener together and is usually lower, because most hardeners contain less bio-based carbon. Figures from the manufacturer's technical datasheets. The Crystal Clear Epoxy figure is tested to ASTM D6866.
CMR means carcinogenic, mutagenic or toxic to reproduction.
Technical data from the manufacturer's datasheets, measured at 23 °C unless stated. Always test before use and read the safety data sheet.